Sharp edged Gd2BaCuO5particles addition effect on growth and properties of top-seeded melt-grown GdBa2Cu3O7-δ bulk superconductors

Shinnosuke Ishibashi, Rikako Hagiwara, Sugali Pavan Kumar Naik, Hiraku Ogino, Paweł Pȩczkowski, Shigeyuki Ishida, Hiroshi Eisaki, Naomichi Sakai, Tetsuo Oka, Taichiro Nishio

研究成果: Conference article査読

1 被引用数 (Scopus)

抄録

We report on top-seeded melt growth of GdBa2Cu3O7-δ (GdBCO) bulks added by sharp edged Gd2BaCuO5 nanoparticles (Gd211U) refined by ultrasonication. GdBCO bulks mixed with 30 mol.% of Gd211U were examined to be grown isothermally at different temperatures in a range of 1015 °C-1035 °C using a top-seeded melt growth technique. Magnetic susceptibility measurements show that all samples become superconducting and especially samples grown at 1020°C and 1025°C have a maximum superconducting transition temperature (T c) of 94.5 K. The critical current density (J c) obtained from magnetic hysteresis loops for magnetic fields parallel to the c-axis is up to 65100 A/cm2 (the self-field at 77 K) for a sample grown at 1025 °C, while J c of a GdBCO bulk with conventional Gd211 particles grown at 1025 °C for comparison is 29000 A/cm2 (the self-field at 77 K).

本文言語English
論文番号012022
ジャーナルJournal of Physics: Conference Series
2323
1
DOI
出版ステータスPublished - 2022
イベント34th International Symposium on Superconductivity, ISS 2021 - Virtual, Online
継続期間: 2021 11月 302021 12月 2

ASJC Scopus subject areas

  • 物理学および天文学(全般)

フィンガープリント

「Sharp edged Gd2BaCuO5particles addition effect on growth and properties of top-seeded melt-grown GdBa2Cu3O7-δ bulk superconductors」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル