Solid phase (RE 2BaO 4)-Liquid phase (BaCuO 2) reaction: The way to highly oriented ErBa 2Cu 3O y superconducting thick films on commercial silver substrates

Muralidhar Miryala, Naomichi Sakai, M. Jirsa, S. Tanaka

研究成果: Article

2 引用 (Scopus)

抄録

Using a solid phase-liquid phase reaction we developed a new technology for preparing c-axis oriented thick ErBa 2Cu 3O y (Er-123) films on commercial polycrystalline silver substrates without the need for a buffer layer. The films were processed in Ar-1% pO 2 atmosphere. Using a double-step annealing, thick Er-123 films were grown, with the onset T c of about 92 K. Formation of large flat grains with the preferential c-axis orientation was confirmed by scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray diffraction. The magnetic self-field critical current density at 77 K was above 40 kA/cm 2. This technology requires only a short processing time and thus is appropriate for utilization in long-length RE-123 silver-sheath wire production.

元の言語English
ページ(範囲)2404-2408
ページ数5
ジャーナルCrystal Growth and Design
9
発行部数5
DOI
出版物ステータスPublished - 2009 5 6
外部発表Yes

Fingerprint

Superconducting films
Silver
Thick films
thick films
solid phases
liquid phases
silver
Liquids
Substrates
Buffer layers
sheaths
critical current
buffers
wire
Wire
Annealing
current density
Transmission electron microscopy
atmospheres
X ray diffraction

ASJC Scopus subject areas

  • Chemistry(all)
  • Materials Science(all)
  • Condensed Matter Physics

これを引用

@article{47fa64dcc5f7497599c75a8726df9543,
title = "Solid phase (RE 2BaO 4)-Liquid phase (BaCuO 2) reaction: The way to highly oriented ErBa 2Cu 3O y superconducting thick films on commercial silver substrates",
abstract = "Using a solid phase-liquid phase reaction we developed a new technology for preparing c-axis oriented thick ErBa 2Cu 3O y (Er-123) films on commercial polycrystalline silver substrates without the need for a buffer layer. The films were processed in Ar-1{\%} pO 2 atmosphere. Using a double-step annealing, thick Er-123 films were grown, with the onset T c of about 92 K. Formation of large flat grains with the preferential c-axis orientation was confirmed by scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray diffraction. The magnetic self-field critical current density at 77 K was above 40 kA/cm 2. This technology requires only a short processing time and thus is appropriate for utilization in long-length RE-123 silver-sheath wire production.",
author = "Muralidhar Miryala and Naomichi Sakai and M. Jirsa and S. Tanaka",
year = "2009",
month = "5",
day = "6",
doi = "10.1021/cg8012987",
language = "English",
volume = "9",
pages = "2404--2408",
journal = "Crystal Growth and Design",
issn = "1528-7483",
publisher = "American Chemical Society",
number = "5",

}

TY - JOUR

T1 - Solid phase (RE 2BaO 4)-Liquid phase (BaCuO 2) reaction

T2 - The way to highly oriented ErBa 2Cu 3O y superconducting thick films on commercial silver substrates

AU - Miryala, Muralidhar

AU - Sakai, Naomichi

AU - Jirsa, M.

AU - Tanaka, S.

PY - 2009/5/6

Y1 - 2009/5/6

N2 - Using a solid phase-liquid phase reaction we developed a new technology for preparing c-axis oriented thick ErBa 2Cu 3O y (Er-123) films on commercial polycrystalline silver substrates without the need for a buffer layer. The films were processed in Ar-1% pO 2 atmosphere. Using a double-step annealing, thick Er-123 films were grown, with the onset T c of about 92 K. Formation of large flat grains with the preferential c-axis orientation was confirmed by scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray diffraction. The magnetic self-field critical current density at 77 K was above 40 kA/cm 2. This technology requires only a short processing time and thus is appropriate for utilization in long-length RE-123 silver-sheath wire production.

AB - Using a solid phase-liquid phase reaction we developed a new technology for preparing c-axis oriented thick ErBa 2Cu 3O y (Er-123) films on commercial polycrystalline silver substrates without the need for a buffer layer. The films were processed in Ar-1% pO 2 atmosphere. Using a double-step annealing, thick Er-123 films were grown, with the onset T c of about 92 K. Formation of large flat grains with the preferential c-axis orientation was confirmed by scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray diffraction. The magnetic self-field critical current density at 77 K was above 40 kA/cm 2. This technology requires only a short processing time and thus is appropriate for utilization in long-length RE-123 silver-sheath wire production.

UR - http://www.scopus.com/inward/record.url?scp=66249124596&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=66249124596&partnerID=8YFLogxK

U2 - 10.1021/cg8012987

DO - 10.1021/cg8012987

M3 - Article

AN - SCOPUS:66249124596

VL - 9

SP - 2404

EP - 2408

JO - Crystal Growth and Design

JF - Crystal Growth and Design

SN - 1528-7483

IS - 5

ER -