Superconducting Performance, Microstructure and SEM by EDX Analysis of IG Processed YBa2Cu3Oy Bulk Superconductors by Top and Interior Seeding Methods

N. Ide, M. Muralidhar, M. Radusovska, P. Diko, M. Jirsa, M. Murakami

研究成果: Conference article

抜粋

The top-seeded and interior seeded methods, together with infiltration growth (IG) technique were used to produce YBa2Cu3Oy (Y-123) samples with Y2BaCuO5 (Y-211) secondary phase particles. Tc (onset) was around 91.5. K. When interior seeding process was used, a complete growth of Y-123 single grain starting at the lower part of the bulk was observed by optical microscopy. The Y-211 particles dispersion was quite uniform in lower and upper parts of the samples, both in the a- and c-axis growth sectors, both at the beginning and end of the grain growth. In the sample produced by infiltration growth and interior seeding the critical current density at 77 K with H//c-axis was 44,000 A/cm2 and 7,750 A/cm2 in self-field and 2 T, respectively. It is a good basis for optimization of processing conditions, which can further improve the superconductor's performance and enable to grow large-size Y-123 bulks.

元の言語English
記事番号012053
ジャーナルJournal of Physics: Conference Series
871
発行部数1
DOI
出版物ステータスPublished - 2017 7 26
イベント29th International Symposium on Superconductivity, ISS 2016 - Tokyo, Japan
継続期間: 2016 12 132016 12 15

ASJC Scopus subject areas

  • Physics and Astronomy(all)

フィンガープリント Superconducting Performance, Microstructure and SEM by EDX Analysis of IG Processed YBa<sub>2</sub>Cu<sub>3</sub>O<sub>y</sub> Bulk Superconductors by Top and Interior Seeding Methods' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用