Superconducting properties of sintered bulk MgB2 prepared from hexane-mediated high-energy-ultra-sonicated boron

S. S. Arvapalli, M. Miryala, P. Sunsanee, M. Jirsa, M. Murakami



Recently, novel low cost techniques have been employed to improve critical current density of MgB2. Ultra-sonication is one such technique. We report on the influence of hexane dispersant on particle size of ultra-sonicated cheap commercial boron and the superconducting properties of MgB2 bulks prepared using this new precursor. XRD showed major peaks corresponding to MgB2, with small fractions of MgO and unreacted Mg. Tc was close to 39 K, with a sharp transition. The highest Jc was found in the sample with boron ultra-sonicated for 30 min as high as 375, 328, and 270 kA/cm2 at 10, 15, and 20 K, respectively. SEM analysis revealed tiny particles and layers randomly dispersed in the microstructure, while EDX indicated that these particles were secondary phases of Mg, B, and O. Flux pinning diagrams showed the peak of normalized pinning force located close to b = 0.2, depicting dominance of grain boundary pinning mechanism.

ジャーナルMaterials Science and Engineering B: Solid-State Materials for Advanced Technology
出版ステータスPublished - 2021 3

ASJC Scopus subject areas

  • 材料科学(全般)
  • 凝縮系物理学
  • 材料力学
  • 機械工学


「Superconducting properties of sintered bulk MgB<sub>2</sub> prepared from hexane-mediated high-energy-ultra-sonicated boron」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。