抄録
Joining of different Y-Ba-Cu-O bulk samples was performed using Er-Ba-Cu-O and Ag added Y-Ba-Cu-O sintered plates. In both cases, a small dip in the trapped field distribution was observed at the joint region due to the poor superconducting properties. However, the trapped field distribution of the sample joined with Ag added Y-Ba-Cu-O using refined Y2BaCuO 5 powders showed a single peak, which was similar to that of a single grain bulk superconductor.
| 元の言語 | English |
|---|---|
| ページ（範囲） | 437-440 |
| ページ数 | 4 |
| ジャーナル | Physica C: Superconductivity and its Applications |
| 巻 | 392-396 |
| 発行部数 | PART 1 |
| DOI | |
| 出版物ステータス | Published - 2003 10 |
| 外部発表 | Yes |
Fingerprint
ASJC Scopus subject areas
- Condensed Matter Physics
これを引用
Welding of different Y-Ba-Cu-O blocks. / Iida, K.; Yoshioka, J.; Sakai, Naomichi; Murakami, Masato.
：: Physica C: Superconductivity and its Applications, 巻 392-396, 番号 PART 1, 10.2003, p. 437-440.研究成果: Article
}
TY - JOUR
T1 - Welding of different Y-Ba-Cu-O blocks
AU - Iida, K.
AU - Yoshioka, J.
AU - Sakai, Naomichi
AU - Murakami, Masato
PY - 2003/10
Y1 - 2003/10
N2 - Joining of different Y-Ba-Cu-O bulk samples was performed using Er-Ba-Cu-O and Ag added Y-Ba-Cu-O sintered plates. In both cases, a small dip in the trapped field distribution was observed at the joint region due to the poor superconducting properties. However, the trapped field distribution of the sample joined with Ag added Y-Ba-Cu-O using refined Y2BaCuO 5 powders showed a single peak, which was similar to that of a single grain bulk superconductor.
AB - Joining of different Y-Ba-Cu-O bulk samples was performed using Er-Ba-Cu-O and Ag added Y-Ba-Cu-O sintered plates. In both cases, a small dip in the trapped field distribution was observed at the joint region due to the poor superconducting properties. However, the trapped field distribution of the sample joined with Ag added Y-Ba-Cu-O using refined Y2BaCuO 5 powders showed a single peak, which was similar to that of a single grain bulk superconductor.
KW - (1 1 0)/(1 1 0) joint
KW - Er-Ba-Cu-O solder
KW - Silver added Y-Ba-Cu-O solder
KW - Superconducting joint
UR - http://www.scopus.com/inward/record.url?scp=0042784890&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=0042784890&partnerID=8YFLogxK
U2 - 10.1016/S0921-4534(03)01162-6
DO - 10.1016/S0921-4534(03)01162-6
M3 - Article
AN - SCOPUS:0042784890
VL - 392-396
SP - 437
EP - 440
JO - Physica C: Superconductivity and its Applications
JF - Physica C: Superconductivity and its Applications
SN - 0921-4534
IS - PART 1
ER -